Low pressure die casting
|Delivery Time||20~30 workdays|
ASTM, DIN, JIS, EN, ISO, GB
Bubble Wrap, Carton, Wooden Case, Pallet
Low pressure casting can adopt all kinds of mold, the working temperature of non-metal mold is generally room temperature, without special requirements, and the working temperature of metal mold has certain requirements. Such as low pressure casting aluminum alloy, metal mold temperature control in commonly 200 ~ 250 ℃, pouring complicated thin-walled parts, can be as high as 300 ~ 350 ℃. It is proved by practice that the casting temperature is lower and better on the premise of making the casting.
When using aluminum ingot and intermediate alloy for melting, first load aluminum, then add intermediate alloy.
When smelting with prefabricated alloy ingots, prefabricated ingots are loaded first and then supplemented with the required amount of aluminum and intermediate alloys. When the burden is made up of billet and aluminum ingot, the largest part of the burden is first melted.
When the furnace is large enough to hold several furnace materials at the same time, the furnace shall be first loaded with elements of a similar melting point.
Flows that burn easily and have low melting points, such as magnesium and zinc, should be added at the end.
A portion of the aluminium liquid should be left in the crucible to accelerate the next furnace melting while continuing to melt.
When using the coating flux, the melting agent should be added at the beginning of the furnace material melting.
Packaging & Delivery
Office & Factory
1. How many pieces are usually suitable for casting?
Minimum order quantity is 100. MOQ varies according on weight, casting method and difficulty.
2. What kind of material do you usually use?
A356(ZL101A) and A380(YL112).
|Alloy Grades||Alloy Code||Mechanical Properties|
(Different by casting methods)
3. What about the wall thickness of the casting products?
For low pressure & gracity & sand casting: appr.5mm;
For die casting: ≥2mm.
If you have any other questions, please feel free to ask.